Status of AASHTO Materials Standards and Test Methods—August 2017

64 Pages·2016·1.58 MB·English

Status of AASHTO Materials Standards and Test Methods—August 2017
This document shows all materials specifications, practices, and test methods that have been published as part of the AASHTO Standard
Specifications for Transportation Materials and Methods of Sampling and Testing from its first publication in 1931 through the most recent
edition.
The chart on the following pages shows each AASHTO standard, in numerical order. Information includes the standard’s original and current
titles, the year it was adopted, and its current status. Active AASHTO standards are shown with a white background; standards which are no
longer active are shown with a gray background. For standards that are no longer active, the chart also shows the date the standard was
discontinued, as well as the reason for its discontinuation, if known. If a substitute standard—either from AASHTO or another organization—has
been identified to be used instead, its number is also provided. Finally, the Notes column contains any additional relevant information about the
publication history of the standard.
AASHTO Standards
AASHTO materials standards consist of a single letter indicating the standard type and a one- to three-digit number uniquely identifying the
standard. This is followed by second number indicating the date of most recent revision and, if applicable, review. These dates change frequently
and are not shown in this list.
Standard Types
Standard types are represented by a one-letter abbreviation for full standards. The letter “P” is added for provisional standards, which are
listed separately for Part 3. The abbreviations for full standard types are as follows:
 M (Materials)
 R (PRactice)
 T (Test)
Standard Numbers
Standard numbers are sequential within standard type.
Status of AASHTO Materials Standards and Test Methods—August 2017
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 1 Stone for Telford Base Course Stone for Telford Base Course 1924 Discontinued 1942
and Resonstructed Base and Reconstructed Base
Course Course
M 2 Broken Stone for Waterbound Crushed Stone for 1924 Discontinued 1938
Base Course Waterbound Base Course
M 3 Broken Slag for Waterbound Crushed Slag for Waterbound 1924 Discontinued 1938
Base Course Base Course
M 4 Broken Stone for Bituminous Crushed Stone for Bituminous 1926 Discontinued 1938
Base Course Base Course
M 5 Portland Cement Portland Cement 1930 Discontinued 1942
M 6 Fine Aggregate for Portland Fine Aggregate for Hydraulic 1924 Active
Cement Concrete Pavement or Cement Concrete
Base Course, Highway Bridges
and Incidental Structures
M 6a Mortar Sand Mortar Sand 1924 Renumbered 1935 Renumbered as M 45
M 7 Broken Stone for Portland Crushed Stone for Portland 1924 Discontinued 1938
Cement Concrete Base Cement Concrete Base
Course Course
M 8 [Title unknown—Never printed] Unused This number was
likely used for a
standard that was
proposed but not
adopted in the
1920s. No record of
its content remains.
M 9 Broken Stone for Waterbound Crushed Stone for 1924 Discontinued 1938
Macadam Surface Course Waterbound Macadam
Surface Course
M 10 Broken Slag for Waterbound Crushed Slag for Waterbound 1924 Discontinued 1938
Macadam Surface Course Macadam Surface Course
M 11 Broken Stone for Bituminous Crushed Stone for Bituminous 1924 Discontinued 1938
Macadam Surface Course Macadam Surface Course
M 12 Broken Slag for Bituminous Crushed Slag for Bituminous 1924 Discontinued 1938
Macadam Surface Course Macadam Surface Course
M 13 Broken Stone for Bituminous Crushed Stone for Bituminous 1926 Discontinued 1938
Concrete Surface Course Concrete Surface Course
M 14 Broken Slag for Bituminous Crushed Slag for Bituminous 1924 Discontinued 1938
Concrete Surface Course Concrete Surface Course
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 15 Broken Stone for Portland Crushed Stone for Portland 1924 Discontinued 1938
Cement Concrete Surface Cement Concrete Surface
Courses, Highway Bridges and Courses, Highway Bridges and
Incidental Incidental
M 16 Broken Slag for Portland Crushed Slag for Portland 1924 Discontinued 1938
Cement Concrete Base and Cement Concrete Base and
Surface Course Surface Course
M 17 Mineral Filler Mineral Filler for Bituminous 1924 Active
Paving Mixtures
M 18 Oil Asphalt Filler Type A Oil Asphalt Filler 1924 Discontinued 1978
M 19 Asphalt Filler Type B Asphalt Filler Type B 1924 Discontinued 1935
M 20 Asphalt Cement (Prepared Penetration-Graded Asphalt 1924 Discontinued 2009 Lack of use
from Petroleum)—Penetration Cement
Grades 30 to 40, 40 to 50, 50
to 60, 60 to 70
M 21 Asphalt Cement (Prepared Asphalt Cement (Prepared 1924 Discontinued 1935
from Petroleum)—Penetration from Petroleum)—Penetration
Grades 85 to 100, 100 to 120, Grades 85 to 100, 100 to 120,
120 to 150 120 to 150
M 22 Asphalt Cement (Prepared Asphalt Cement, Prepared 1924 Discontinued 1961 Did not appear in
from Native Asphalt)— from Native Asphalt, Grades 1961 edition
Penetration Grades 30 to 40, 30-40, 40-50, 60-70
40 to 50, 50 to 60, 60 to 70
M 23 Asphalt Cement (Prepared Asphalt Cement, Prepared 1924 Discontinued 1942
from Native Asphalt)— from Native Asphalt, Grades
Penetration Grades 85 to 100, 85-100, 100-120, 120-150
100 to 120, 120 to 150
M 24 Tar for Surface Treatment Tar for Surface Treatment 1924 Discontinued 1935
(Cold Application) (Cold Application)
M 25 Tar for Surface Treatment (Hot Tar for Surface Treatment (Hot 1924 Discontinued 1935
Application) Application)
M 26 Tar for Use in the Maintenance Tar for Use in the Maintenance 1924 Discontinued 1935
of Cracks and for Sealing of Cracks and for Sealing
Joints in Concrete Roads Joints in Concrete Roads
M 27 Tar Cement Tar Cement 1924 Discontinued 1935
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 28 [Title unknown—Never printed] Unused This number was
likely used for a
standard that was
proposed but not
adopted in the
1920s. No record of
its content remains.
M 29 Sand for Bituminous Mixtures Fine Aggregate for Bituminous 1924 Active
Paving Mixtures
M 30 Wire Rope and Fittings for Metallic-Coated Steel Wire 1926 Active
Highway Guard Rail Rope and Fittings for Highway
Guardrail
M 31 Billet-Steel Concrete Deformed and Plain Billet- 1924 Converted 1997 Replaced by dual-unit
Reinforcement Bars Steel Bars for concrete standard M 31M/M 31
Reinforcement
M 31M/M 31 Deformed and Plain Billet- Deformed and Plain Carbon 1995 Active
Steel Bars for Concrete and Low-Alloy Steel Bars for
Reinforcement Concrete Reinforcement
M 31M Deformed and Plain Billet- Deformed and Plain Billet- 1982 Converted 1997 Replaced by dual-unit
Steel Bars for Concrete Steel Bars for Concrete standard M 31M/M 31
Reinforcement [Metric] Reinforcement [Metric]
M 32 Cold Drawn Steel Wire Fabric Steel Wire, Plain, for Concrete 1924 Converted 1995 Replaced by dual-unit
for Concrete Reinforcement Reinforcement standard M 32M/M 32
M 32M/M 32 Steel Wire, Plain, for Concrete Steel Wire, Plain, for Concrete 1994 Active
Reinforcement Reinforcement
M 33 Pre-molded Expansion Joints Premolded Expansion Joint 1924 Active Did not appear in
Filler for Concrete (Bituminous 1935 edition, but
Type) was back in 1938
edition
M 34 White Traffic (Zone) Paint White Traffic (Zone) Paint 1927 Discontinued 1942
(Ready Mixed) for Brick and (Ready-Mixed) for Bituminous
Bituminous Pavements Pavements
M 35 White Traffic (Zone) Paint White Traffic (Zone) Paint 1927 Discontinued 1942
(Ready Mixed) for Brick and (Ready-Mixed) for Brick and
Concrete Pavements Concrete Pavements
M 36 Base Metal for Corrugated Corrugated Steel Pipe, Metallic- 1932 Active Published as dual-
Metal Sheets for Culverts Coated, for Sewers and Drains unit standard M
36M/M 36 from 1983-
96 and metric
standard M 36M
from 1997-99
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 36M/M 36 Corrugated Steel Pipe, Metallic-Corrugated Steel Pipe, Metallic- 1983 Converted 1997 Reverted to metric
Coated, for Sewers and Drains Coated, for Sewers and Drains standard M 36M
M 36M Corrugated Steel Pipe, Metallic-Corrugated Steel Pipe, Metallic- 1996 Converted 2000 Reverted to U.S.-unit
Coated, for Sewers and Drains Coated, for Sewers and Drains standard M 36
M 37 Gravel for Portland Cement Gravel for Portland Cement 1929 Discontinued 1938
Concrete Pavements or Bases, Concrete Pavements or Bases,
Highway Bridges and Highway Bridges and
Incidental Structures Incidental Structures
M 38 Asphalt Emulsion (Slow- Asphalt Emulsion (Slow- 1930 Discontinued 1935
Breaking Type) Breaking Type)
M 39 High-Early-Strength Portland High-Early-Strength Portland 1930 Discontinued 1942
Cement Cement
M 40 Paving Brick Paving Brick 1932 Discontinued 1971 First published in
1931, but with no
date of adoption.
M 41 Reinforced-Concrete Culvert Reinforced Concrete Culvert 1935 Discontinued 1961 First published in
Pipe Pipe 1931, but with no
date of adoption.
M 42 Rail-Steel Concrete Rail-Steel Deformed and Plain 1933 Converted 1988 Replaced by dual-unit
Reinforcement Bars Bars for Concrete standard M 42M/M 42
Reinforcement
M 42M/M 42 Rail-Steel Deformed and Plain Rail-Steel Deformed and Plain 1988 Discontinued 2003 Combined with M
Bars for Concrete Bars for Concrete 53M/M 53 to become M
Reinforcement Reinforcement 322M/M 322
M 43 Sizes of Aggregates Sizes of Aggregate for Road 1935 Active
and Bridge Construction
M 44 Crushed Slag for Bituminous Crushed Slag for Bituminous 1935 Discontinued 1938
Concrete Base Course Concrete Base Course
M 45 Mortar Sand Aggregate for Masonry Mortar 1924 Active Formerly M 6a
M 46 Premolded Asphalt Plank Asphalt Plank 1935 Discontinued 1993 Lack of use
M 47 Emulsified Asphalt for Open Emulsified Asphalt 1935 Discontinued 1950 Moved specification to
Graded Coarse Aggregate Standard Specification
Plant Mixtures for Highway Bridges
M 48 Emulsified Asphalt for Open Emulsified Asphalt 1935 Discontinued 1950 Moved specification to
Graded Coarse Aggregate Standard Specification
Mixed-in-Place Construction for Highway Bridges
M 49 Emulsified Asphalt for Summer Emulsified Asphalt 1935 Discontinued 1950 Moved specification to
Use in Bituminous Concrete Standard Specification
Mixtures for Repair Work for Highway Bridges
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 50 Emulsified Asphalt for Winter Emulsified Asphalt 1935 Discontinued 1950 Moved specification to
Use in Bituminous Concrete Standard Specification
Mixtures for Repair Work for Highway Bridges
M 51 Emulsified Asphalt for Emulsified Asphalt 1935 Discontinued 1950 Moved specification to
Penetration Macadam and Standard Specification
Surface Treatment Work for Highway Bridges
M 52 Tar for Use in Road Tar for Use in Road 1937 Discontinued 1988 Lack of use
Construction Construction
M 53 Axle-Steel Concrete Axle-Steel Deformed and Plain 1937 Converted 1989 Replaced by dual-unit
Reinforcement Bars Bars for Concrete standard M 53M/M 53
Reinforcement
M 53M/M 53 Axle-Steel Deformed and Plain Axle-Steel Deformed and Plain 1989 Discontinued 2003 Combined with M
Bars for Concrete Bars for Concrete 42M/M 42 to become M
Reinforcement Reinforcement 322M/M 322
M 54 Fabricated Bar or Rod Mats for Fabricated Bar or Rod Mats for 1937 Converted 1986 Replaced by dual-unit
Concrete Reinforcement Concrete Reinforcement standard M 54M/M 54
M 54M/M 54 Fabricated Steel Bar or Rod Welded Deformed Steel Bar 1986 Active
Mats for Concrete Mats for Concrete
Reinforcement Reinforcement
M 55 Welded Wire Fabric for Steel Welded Wire Fabric, 1937 Converted 1994 Replaced by dual-unit
Concrete Reinforcement Plain, for Concrete standard M 55M/M 55
Reinforcement
M 55M/M 55 Steel Welded Wire Fabric, Steel Welded Wire 1994 Active
Plain, for Concrete Reinforcement, Plain, for
Reinforcement Concrete
M 56 Materials for Stabilized Base Materials for Stabilized Base 1938 Discontinued 1950 Moved specification to
Course Course Standard Specification
for Highway Bridges
M 57 Materials for Use in Materials for Embankments 1938 Active
Embankment Construction and Subgrades
M 58 Premolded Expansion Joint Preformed Expansion Joint 1938 Discontinued 1955
Filler for Concrete Fillers for Concrete (Cork, Self-
(Nonextruding and Resilient expanding Cork, Sponge
Types) Rubber and Cork-rubber
Types)
M 59 Premolded Bituminous Fiber Prefirmed Expansion Joint 1938 Discontinued 1955
Expansion Joint Filler for Filler for Concrete (Bituminous
Concrete Cellular Type)
M 60 Moderate Sulphate Resisting Moderate Sulphate Resisting 1938 Discontinued 1942
Portland Cement Portland Cement
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 61 Materials for Stabilized Surface Materials for Stabilized Surface 1938 Discontinued 1950 Moved specification to
Course Course Standard Specification
for Highway Bridges
M 62 Crushed Stone, Crushed Slag Crushed Stone, Crushed Slag 1938 Discontinued 1978
and Crushed Gravel for Dense- and Crushed Gravel for Dense-
Graded Bituminous Road and Graded Bituminous Road and
Plant-Mix Surface Course Plant-Mix Surface Course
M 63 Crushed Gravel for Open- Crushed Stone, Crushed Slag 1938 Discontinued 1978
Graded Bituminous Road-Mix and Crushed Gravel for Open-
Surface Course Graded Bituminous Road-Mix
Surface Course
M 64 Cast-Iron Culvert Pipe Ductile Iron Culvert Pipe 1938 Discontinued 1990
M 65 Vitrified Clay Culvert Pipe Vitrified Clay Culvert Pipe, 1938 Discontinued 1997 Lack of use
Extra Strength, Standard
Strength and Perforated
M 66 Drain Tile Drain Tile 1938 Discontinued 1961 Did not appear in
1961 edition
M 67 Green Graphite Bridge Paint Foliage Green Bridge Paint 1938 Discontinued 1992 Lack of use Discontinued in
1947; reinstated in
1950; discontinued
again in 1992
M 68 Black Bridge Paint Black Paint for Bridges or 1938 Discontinued 1992 Lack of use Discontinued in
Timber Structures 1947; reinstated in
1950; discontinued
again in 1992
M 69 Aluminum Paint (Paste-Mixing Aluminum Paint 1938 Discontinued 2006 Obsolete
Vehicle)
M 70 White and Tinted Ready-Mixed White and Tinted Ready-Mix 1938 Discontinued 1992 Lack of use
Paint (Lead and Zinc Base) Oil Base Paint
M 71 Red Lead (Dry and Paste-in- Red Lead (Dry and Paste-in- 1938 Discontinued 1971
Oil) and Paint Made Therefrom Oil) and Paint Made Therefrom
M 72 Red Lead Ready-Mixed Paint Red Lead Ready-Mixed Paint 1938 Discontinued 1992 Lack of use
M 73 Cotton Mats for Curing Cotton Mats for Curing 1938 Discontinued 1970
Concrete Pavements Concrete Pavements
M 74 Subgrade Paper Subgrade Paper 1938 Discontinued 1972 Lack of use
M 75 Crushed Stone and Crushed Crushed Stone and Crushed 1938 Discontinued 1978
Slag for Base Course Slag for Base Course
M 76 Crushed Stone and Crushed Crushed Stone and Crushed 1938 Discontinued 1978
Slag for Bituminous Concrete Slag for Bituminous Concrete
Base Course Base Course
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 77 Crushed Stone and Crushed Crushed Stone and Crushed 1938 Discontinued 1978
Slag for Waterbound Surface Slag for Waterbound Surface
Course Course
M 78 Crushed Stone and Crushed Crushed Stone and Crushed 1938 Discontinued 1978
Slag for Bituminous Macadam Slag for Bituminous Macadam
Surface Course Surface Course
M 79 Crushed Stone and Crushed Crushed Stone and Crushed 1938 Discontinued 1978
Slag for Bituminous Concrete Slag for Bituminous Concrete
Surface Course Surface Course
M 80 Coarse Aggregate for Portland Coarse Aggregate for 1938 Active
Cement Concrete Hydraulic Cement Concrete
M 81 Cut-Back Asphalt, Rapid- Cutback Asphalt (Rapid-Curing 1938 Active
Curing Type Type)
M 82 Cut-Back Asphalt, Medium- Cutback Asphalt (Medium- 1938 Active
Curing Type Curing Type)
M 83 Liquefier Liquefier 1938 Discontinued 1971
M 84 Granulated Slag for Bedding Granulated Slag for Bedding 1938 Discontinued 1971
Course of Brick Pavements Course
M 85 Portland Cement Portland Cement 1942 Active
M 86 Concrete Sewer Pipe Concrete Sewer, Storm Drain, 1942 Converted 2005 Replaced with dual-unit
and Culvert Pipe standard M 86M/M 86
M 86M/ M 86 Concrete Sewer, Storm Drain, Nonreinforced Concrete 2004 Active
and Culvert Pipe Sewer, Storm Drain, and
Culvert Pipe
M 86M Concrete Sewer, Storm Drain, Concrete Sewer, Storm Drain, 1981 Converted 2005 Replaced with dual-unit
Culvert Pipe [Metric] and Culvert Pipe (Metric) standard M 86M/M 86
M 87 Reinforced Concrete Sewer Reinforced Concrete Sewer 1942 Discontinued 1961
Pipe Pipe
M 88 Emulsified Ashpalt (For the Emulsified Ashpalt 1942 Discontinued 1950 Moved specification to
Surface Treatment of Roads) Standard Specification
for Highway Bridges
M 89 Mixed Asphalt and Mineral Mixed Asphalt and Mineral 1942 Discontinued 1971
Filler Filler
M 90 Redwood Board Expansion Redwood Board Expansion 1942 Discontinued 1970
Joint Filler for Concrete Joint Filler for Concrete
M 91 Sewer Brick (Made from Clay Sewer and Manhole Brick 1942 Discontinued 2011 Replaced by ASTM C32
or Shale) (Made from Clay or Shale)
M 92 Sieves for Testing Purposes, Wire-Cloth Sieves for Testing 1942 Discontinued 2016 Replaced by ASTM E11-Did not appear in
Wire Cloth Sieves, Round-Hole Purposes 15 1961 edition
and Square-Hole Screens or
Sieves
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 93 Thermometers Thermometers 1942 Discontinued 1950
M 94 Steel for Bridges and Buildings Steel for Bridges and Buildings 1939 Discontinued 1966 Did not appear in
1950 or 1955
editions
M 95 Structural Silicon Steel Structural Silicon Steel 1939 Discontinued 1966 Did not appear in
1950 or 1955
editions
M 96 Structural Nickel Steel Structural Nickel Steel 1939 Discontinued 1966 Did not appear in
1950 or 1955
editions
M 97 Structural Rivet Steel Structural Rivet Steep 1939 Discontinued 1970 Incorporated into M 228 Did not appear in
1950 or 1955
editions
M 98 High-Strength Structural Rivet High-Strength Structural Rivet 1941 Discontinued 1970 Incorporated into M 228 Did not appear in
Steel Steel 1950 or 1955
editions
M 99 Wrought Iron Plates Wrought Iron Plates 1939 Discontinued 1971 Did not appear in
1950 or 1955
editions
M 100 Rolled Wrought Iron Shapes Rolled Wrought Iron Shapes 1939 Discontinued 1971 Did not appear in
and Bars and Bars 1950 or 1955
editions
M 101 Welded Wrought-Iron Pipe Welded Wrought-Iron Pipe 1939 Discontinued 1971
M 102 Carbon-Steel Forgings for Steel forgings, Carbon and 1940 Converted 1997 Replaced with dual-unit
General Industrial Use Alloy, for General Industrial standard M 102M/M
Use 102
M 102M/M Steel forgings, Carbon and Steel Forgings, Carbon, and 1996 Active
102 Alloy, for General Industrial Alloy, for General Industrial
Use Use
M 103 Carbon-Steel Castings for Mild- to Medium-Strength 1939 Converted 1990 Replaced with dual-unit
Miscellaneous Industrial Uses Carbon-Steel Castings for standard M 103M/M
General Applications 103
M 103M/M Steel Castings, Carbon, for Steel Castings, Carbon, for 1989 Active
103 General Application General Application
M 104 Chromium Alloy-Steel Castings Chromium Alloy-Steel Castings 1939 Discontinued 1950
M 105 Gray Iron Castings Gray Iron Castings 1941 Active
M 106 Malleable Iron Castings Malleable Iron Castings 1935 Discontinued 1976 Being generally
unavailable except as
plumbing fixtures
Standard Year Year Reason Discontinued (If
Number Original Title Current/Final Title Adopted Status Discontinued Known) Other Notes
M 107 Bronze Castings for Turntables Bronze Castings for Bridges 1940 Discontinued 2011 Replaced by ASTM B22
and Movable Bridges and for and Turntables
Bearing and Expansion Plates
of Fixed Bridges
M 108 Rolled Copper-Alloy Bearing Wrought Copper-Alloy Bearing 1940 Discontinued 2011 Replaced by ASTM
and Expansion Plates for and Expansion Plates and B100
Bridge and Other Structural Sheets for Bridge and Other
Use Structural Use
M 109 Lake Copper Wire Bars, Lake Copper Wire Bars, 1935 Discontinued 1950
Cakes, Slabs, Billets, Ingots, Cakes, Slabs, Billets, Ingots,
and Ingot Bars and Ingot Bars
M 110 Electrolytic Copper Wire Bars, Electrolytic Copper Wire Bars, 1935 Discontinued 1950
Cakes, Slabs, Billets, Ingots, Cakes, Slabs, Billets, Ingots,
and Ingot Bars and Ingot Bars
M 111 Zinc (Hot-Galvanized Coatings Zinc (Hot-Dip Galvanized) 1935 Converted 1999 Replaced by dual-unit
on Structural Steel Shapes, Coatings on Iron and Steel standard M 111M/M
Plates and Bars, and Their Products 111
Products
M 111M/M Zinc (Hot-Dip Galvanized) Zinc (Hot-Dip Galvanized) 1999 Active
111 Coatings on Iron and Steel Coatings on Iron and Steel
Products Products
M 112 Pig Lead Pig Lead 1940 Discontinued 1978
M 113 Rolled Zinc Rolled Zinc 1939 Discontinued 1978
M 114 Building Brick (Made from Clay Building Brick (Solid Masonry 1941 Discontinued 2011 Replaced by ASTM C62
or Shale) Units Made from Clay or
Shale)
M 115 Asphalt for Dampproofing and Asphalt Used in Damp- 1942 Discontinued 1993 Lack of use
Waterproofing Proofing and Waterproofing
M 116 Primer for Use with Asphalt in Asphalt Primer Used in 1942 Discontinued 1993 Lack of use
Dampproofing and Roofing, Damp-Proofing, and
Waterproofing Waterproofing
M 117 Woven Cotton Fabrics Bitumen-Saturated Cotton 1940 Discontinued 1993 Lack of use
Saturated with Bituminous Fabrics Used in Roofing and
Substances for Use in Waterproofing
Waterproofing
M 118 Coal-Tar Pitch for Roofing, Coal-Tar Bitumen Used in 1942 Discontinued 1997 Lack of use
Dampproofing, and Roofing, Damp-Proofing, and
Waterproofing Waterproofing
M 119 Fire-Refined Copper Other Fire-Refined Copper Other 1935 Discontinued 1950
Than Lake Than Lake
M 120 Slab Zinc (Spelter) Zinc 1937 Discontinued 2011 Replaced by ASTM B6